  SJ101-sintered flux    
 
 Sintered flu >> SJ101-sintered flux
 
  
 
  
产品编号:
2-001
产品名称:
SJ101-sintered flux
    产 品 说 明

Product DescriptionSJ101(Bonded flux)

SJ101 is a bonded type high basic flux with ball form gray granule about 10-60 mesh in size. It can be used on AC or DC power source, and also can be used large current. Its unique features include stable arc, easy slag removal and smooth bead with head appearance. The weld metal shows good toughness at low temperature.

APPLICATIONS:
In combination with H08A. H08MnA. H08MnMoA. H10Mn2 wires, this flux is suitable for welding of low alloy steels for important products, such as boilers, pressure vessels, pipelines, etc. It is also suitable for multiple-wire submerged are welding, especially for butt welding of large diameter vessel with one-pass on both sides.

GUIDELINES FOR USAGE:
1. Dry the flux at 300-350 for 2 hours before use
2. Completely remove rust, oil and dirt from the groove surface prior to welding.
TYPICAL FLUX COMPOSITION RANGE: (%)
SiO2+TiO2 MGO+CaO Al2O3+MnO CaF2 others
15-25 25-35 20-30 -15 -10

TYPICAL MECHANICAL PROPERTIES OF WELDING METAL(GB/T5293-99 F5A4-H10Mn2)
Test Item
MPa
MPa
% Akv(J)
-40
Guarantee Value 480-650 ≥ 380 ≥ 22 ≥ 27
Test Value 573 448 33.6 61\48\51.

点击数:8519  录入时间:2012/3/16 【打印此页】 【关闭
 